Bayflex® 906 (26 pcf)
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KiLkst_Bayflex-906-26-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayflex 906 is a fully compounded, water-blown, polyether-based polyurethane system consisting of two liquid components. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Bayflex 906 system was developed for use in a wide variety of applications requiring a microcellular core and a tough, abrasion-resistant outer surface. Examples of possible applications include appliance handles, office chair armrests, and dunnage strips. As with any product, use of the Bayflex 906 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shaw A, 12.7mm) | 57 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 12.7 mm) | 2.70 | MPa | ASTM D412 |
| Tensile Elongation (Break, 12.7 mm) | 210 | % | ASTM D412 |
| Tear Strength 1(12.7 mm) | 13.3 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components 2 | |||
| Component a | Mixing ratio by weight: 73 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 800 mPa Flash Point, PMCC: 213°C NCO: 22.6 to 23.1 wt% Part B Type: Polyol Specific Gravity @ 25°C: 1.02 Viscosity @25°C: 1100 mPa-s Flash Point, PMCC: 121°C Water: 0.60 wt% max Hydroxyl Number: 194: mg KOH/g Material Temperatures: 25 to 40°CMold Temperature: 55 to 65°CDemold Time, 0.25 in thickness: 3.5 minLinear Shrinkage at 0.50 g/cm³: <0.5%Hand Mix Reactivity at 23°C Cream Time: 50 sec Tack-Free Time: 60 sec Pull Time: 90 sec Free-Rise Density: 11 to 16 lb/ft³ |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 98 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 523S | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| STARFLEX® P 7391 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| Abstron IM11BM | Bhansali Engineering Polymers Limited | ABS | Abstron |
| KumhoSunny PPO HSP8340 | Shanghai KumhoSunny Plastics Co., Ltd. | PPE+PS | KumhoSunny PPO |
| PERLER® N09X4001B00 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |