Ultramid® B3GM35 Q643
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ki9K5L_Ultramid-B3GM35-Q643.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3GM35 Q643 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade. Applications Typical applications include industrial articles requiring medium rigidity and high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation | 5.7 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7960 | -- | MPa | ISO 527-2 |
| Tensile Strength (Break, 23°C) | 123 | -- | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 2.6 | -- | % | ASTM D638 |
| Break, 23°C | 2.7 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7500 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.1 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| -40°C | 40 | -- | J/m | ASTM D256 |
| 23°C | 53 | 130 | J/m | ASTM D256 |
| 23°C | 4.8 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, Unannealed | 198 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 199 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAF479 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Stylac™ A3921 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Ecomass® 1002TU96 | Ecomass Technologies | PEBA-Ether | Ecomass® |
| KRATON® D1118 E | Kraton Polymers LLC | SBC | KRATON® |
| POLYCOMPO PE 7500M | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |