Sunny® PA66 EB130
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KhrcSe_Sunny-PA66-EB130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP reinforced Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 to 0.50 | % | ASTM D955 |
| 23°C | 0.30 to 0.50 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 1.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 160 | MPa | ASTM D638 |
| -- | 160 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.8 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 9210 | MPa | ASTM D790 |
| 50.0 mm Span | 9500 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 203 | MPa | ASTM D790 |
| -- 4 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D256 |
| 23°C | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 230 | °C | ASTM D648, ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 260 | °C | |
| Front Temperature | 255 | °C | |
| Processing (Melt) Temp | 265 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4F 809-SB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Makrolon® ET UV530 | Covestro - Polycarbonates | PC | Makrolon® |
| THERMOLAST® V TV5LVZ (Series: LTP) | KRAIBURG TPE | SEPS | THERMOLAST® V |
| Mylar® D (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| NP Purge™ Series | Noble Polymers | Polyolefin, Unspecified | NP Purge™ |