CoolPoly® E5107
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Cool Polymers, Inc. |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KheSbe_CoolPoly-E5107.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly E series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The E series is electrically conductive and provides inherent EMI/RFI shielding characteristics. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.95 | % | ISO 527-2 |
| Flexural Modulus | 11600 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat | 1100 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 1.4 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 9.0E+7 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM D177C, was tested in accordance with ASTM E1461The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461.Thermal Diffusivity, ASTM E1461: 0.0082 cm²/secInsulation Resistance, EN 50014: 1E7 ohms |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 282 - 299 | °C | |
| Middle Temperature | 288 - 307 | °C | |
| Front Temperature | 293 - 321 | °C | |
| Nozzle Temperature | 293 - 332 | °C | |
| Processing (Melt) Temp | 293 - 332 | °C | |
| Mold Temperature | 135 - 175 | °C | |
| Injection Pressure | 60.0 - 165 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 105 | MPa | |
| Back Pressure | 0.200 - 0.500 | MPa | |
| Screw Speed | 75 - 180 | rpm | |
| Cushion | 5.00 - 13.0 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net VC810 | Polytech & Net Gmbh | EVA | Polytech & Net |
| TOYOBO Urethane A3064D | TOYOBO America, Inc. | PUR-Ether | TOYOBO Urethane |
| Magnobond 6398 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| GELOY™ FXW751SK resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| NORYL™ GFN2 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |