Generic PP Copolymer
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KgesPr_Generic-PP-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.890 - 0.912 | g/cm³ | ASTM D792 |
| 23°C | 0.885 - 0.948 | g/cm³ | ISO 1183 |
| -- | 0.896 - 0.901 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.30 - 30 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.28 - 30 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 2.00 - 55.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.1 - 1.9 | % | ASTM D955 |
| Transverse flow : 23°C | 1.4 - 2.3 | % | ASTM D955 |
| 23°C | 1.1 - 1.8 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.010 - 0.021 | % | ASTM D570 |
| 23°C, 24 hr | 0.046 - 0.21 | % | ISO 62 |
| Saturated, 23°C | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 63 - 106 | ASTM D785 | |
| 23°C | 86 - 96 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 60 - 74 | ASTM D2240 | |
| 23°C | 58 - 70 | ISO 868 | |
| Ball Indentation Hardness | 43.6 - 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 709 - 1720 | MPa | ASTM D638 |
| 23°C | 981 - 1620 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 19.6 - 28.1 | MPa | ASTM D638 |
| Yield, 23°C | 17.9 - 30.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 12.6 - 30.2 | MPa | ASTM D638 |
| Fracture, 23°C | 10.0 - 31.3 | MPa | ISO 527-2 |
| 23°C | 16.1 - 30.3 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.0 - 16 | % | ASTM D638 |
| Yield, 23°C | 1.0 - 13 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 510 | % | ASTM D638 |
| Fracture, 23°C | 3.3 - 410 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 791 - 1480 | MPa | ASTM D790 |
| 23°C | 817 - 1510 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 20.7 - 50.6 | MPa | ASTM D790 |
| 23°C | 17.9 - 40.1 | MPa | ISO 178 |
| Yield, 23°C | 25.2 - 35.9 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 447 - 555 | MPa | ISO 527-3 |
| Tensile Strength (23°C) | 29.0 - 50.4 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 23°C) | 590 - 750 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 - 51 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 5.0 - 81 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 8.0 - 140 | J/m | ASTM D256 |
| 23°C | 3.0 - 52 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 4.5 - 1500 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 2.71 - 40.0 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 17.8 - 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 78.4 - 131 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 72.8 - 115 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 42.9 - 61.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 44.0 - 58.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -45.0 - -5.00 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 134 - 157 | °C | ASTM D1525 |
| -- | 53.6 - 153 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 162 - 167 | °C | ISO 11357-3 |
| -- | 165 - 168 | °C | ASTM D3418 |
| -- | 160 - 165 | °C | ISO 3146 |
| CLTE - Flow | 8.7E-5 - 1.6E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec | 65.0 - 66.5 | °C | UL 746 |
| RTI Imp | 65.0 - 66.4 | °C | UL 746 |
| RTI | 65.0 - 66.4 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 80 - 2.5E+13 | ohms | ASTM D257 |
| -- | 1.0E+2 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 50 - 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 20 - 2.5E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 39 - 40 | kV/mm | ASTM D149 |
| Arc Resistance | 130 - 131 | sec | ASTM D495 |
| Comparative Tracking Index | 594 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 950 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 694 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 - 30 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 3 - 130 | ASTM D2457 | |
| Haze | 0.30 - 41 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.8 - 90.9 | °C | |
| Drying Time | 1.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.21 | % | |
| Suggested Max Regrind | 53 | % | |
| Rear Temperature | 178 - 222 | °C | |
| Middle Temperature | 190 - 228 | °C | |
| Front Temperature | 190 - 234 | °C | |
| Nozzle Temperature | 203 - 238 | °C | |
| Processing (Melt) Temp | 194 - 245 | °C | |
| Mold Temperature | 20.0 - 62.0 | °C | |
| Injection Pressure | 4.05 - 101 | MPa | |
| Holding Pressure | 4.63 - 53.9 | MPa | |
| Back Pressure | 0.188 - 0.750 | MPa | |
| Screw Speed | 49 - 77 | rpm | |
| Clamp Tonnage | 0.98 - 4.5 | kN/cm² | |
| Cushion | 4.76 - 9.53 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP CopolymerThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.9 - 80.6 | °C | |
| Drying Time | 1.5 - 3.0 | hr | |
| Suggested Max Moisture | 0.066 - 0.083 | % | |
| Cylinder Zone 1 Temp. | 194 - 210 | °C | |
| Cylinder Zone 2 Temp. | 200 - 210 | °C | |
| Cylinder Zone 3 Temp. | 200 - 211 | °C | |
| Cylinder Zone 4 Temp. | 200 - 211 | °C | |
| Cylinder Zone 5 Temp. | 209 - 211 | °C | |
| Melt Temperature | 195 - 222 | °C | |
| Die Temperature | 200 - 215 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP CopolymerThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7-7022RF | Spartech Polycom | PC | Spartech |
| Sylvin 2910-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APEX® 302 | Teknor Apex Company | PVC, Flexible | APEX® |
| HiFill® PA6/6 G/CF30 L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Karina CLEAR PVC COMPOUND -E 80/266-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |