4LOY® 10E07200
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | 4Plas |
| Trademark: | 4LOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kg7FVR_4LOY-10E07200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LOY 10E07200 is a Extrusion 65% PC / 35% ABS PC/ABS |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/5 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 52.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.2 | % | ISO 527-2/5 |
| Fracture, 23°C | 50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Melt Temperature | 230 - 260 | °C | |
| Die Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTAMID™ MA3ZK | Marplex Australia Pty. Ltd. | Nylon 66 | ASTAMID™ |
| Axiall PVC 22941 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| KUBE PIR 22402 | KUBE Electronics AG | HDPE | KUBE PIR |
| Lupoy® GN5001RFT | LG Chem Ltd. | PC+ABS | Lupoy® |
| Hostacom EP3307 C11462 | LyondellBasell Industries | PP Copolymer | Hostacom |