Nylux 66-GF33NAT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | Nylux |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KfuNyG_Nylux66GF33NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylux66-GF33NAT is a 33% glass reinforced, heat stabilized PA66 resin suitable applications in which tensile strength and dimensional stability are needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 2.00mm | 0.30 - 0.40 | % | ISO 294-4 |
| Flow : 2.00mm | 0.90 - 1.1 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 205 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 255 | °C | |
| Melting Temperature | 262 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 200 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Daplen™ EE108AE | Borealis AG | TPO | Daplen™ |
| Elastane™ 4721R10 | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Polifor® 5020/V2 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Durez® 33183 | SBHPP | Phenolic | Durez® |