LubriOne™ LB9800-8001 AR Black
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KfmHCt_LubriOne-LB9800-8001-AR-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™Lubricating and wear-resistant polymers are specially used for self-lubricating materials, and their friction coefficient is low, which can improve wear resistance. LubriOne polymers have been proven to reduce friction, noise, vibration, heat generation and improve product durability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C, 3.20mm | 0.10 - 0.30 | % | ASTM D955 |
| Lateral flow : 23°C, 3.20mm | 1.5 - 1.7 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.040 | % | ASTM D570 |
| Saturated, 23°C | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 84 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 3.20 mm) | 12500 | MPa | ISO 527-2/1/5 |
| Tensile Stress | ISO 527-2/1/5 | ||
| Fracture, 23°C, 3.20mm | 145 | MPa | ISO 527-2/1/5 |
| Fracture, 120°C, 3.20mm | 95.0 | MPa | ISO 527-2/1/5 |
| Tensile Strain (Break, 23°C, 3.20 mm) | 3.0 | % | ISO 527-2/1/5 |
| Flexural Modulus 2 | ASTM D790 | ||
| 23°C, 3.20 mm | 10500 | MPa | ASTM D790 |
| 120°C, 3.20 mm | 10400 | MPa | ASTM D790 |
| Flexural Strength 3 | ASTM D790 | ||
| Fracture, 23°C, 3.20mm | 215 | MPa | ASTM D790 |
| Fracture, 120°C, 3.20mm | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 315 | °C | ASTM D648 |
| Glass Transition Temperature | 146 | °C | DSC |
| Melting Temperature | 343 | °C | DSC |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 143°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : > 143°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 2.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | ASTM E1461 | ||
| 60°C 4 | 0.46 | W/m/K | ASTM E1461 |
| 60°C 5 | 1.4 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 1.0E+13 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 160 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 350 - 390 | °C | |
| Mold Temperature | 180 - 200 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | through-plane |
| 5 . | in-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 1082 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| ACCUTECH™ CP0436W30L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| ENFLEX S3190A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Iupital® FX-11J | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| POLYfill PP HJ752 | Polykemi AB | PP, Unspecified | POLYfill |