| The Honeywell Halar® E-Series ECTFE film is a high performance film with excellent mechanical, electrical and release properties. It is non-flammable, and has outstanding chemical resistance. Halar E-Series Film is available in the following colors: Blue, White and Clear. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.28 | ASTM D1894 | |
| With self-dynamics | 0.58 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD | 1860 | MPa | ASTM D882 |
| TD | 1550 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 35.2 | MPa | ASTM D882 |
| TD : Yield | 31.0 | MPa | ASTM D882 |
| MD : Fracture | 71.7 | MPa | ASTM D882 |
| TD : Fracture | 57.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 240 | % | ASTM D882 |
| TD : Fracture | 290 | % | ASTM D882 |
| Water Vapor Transmission Rate (38°C, 100% RH) | 0.098 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 240 | °C | ASTM D3418 |
| Additional Information |
|---|
| Yield: 8245 in²/lbTensile Strength @ Yield, ASTM D 882, MD: 4500 to 5700 psiTensile Strength @ Yield, ASTM D 882, TD: 4000 to 5000 psiTensile Strength @ Break, ASTM D 882, MD: 88000 to 12000 psiTensile Strength @ Break, ASTM D 882, TD: 6200 to 10500 psiElongation @ Break, ASTM 882, MD: 200 to 275%Elongation @ Break, ASTM 882, TD: 250 to 325%Secant Modulus, ASTM D 882, MD: 230000 to 300000 psiSecant Modulus, ASTM D 882, TD: 200000 to 250000 psiGraves Tear (initial), ASTM D 1004, MD: 500 to 600 g/milGraves Tear (initial), ASTM D 1004, TD: 450 to 550 g/milDimensional Stability, ASTM D1204, 300°F, 10 min: <3% shrinkageCoef of Friction, ASTM D1894, Vs Metal - Dynamic: 0.23 to 0.33Coef of Friction, ASTM D1894, Vs Itself - Dynamic: 0.30 to 0.86 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® B121U-51 | Razin™ Engineering Plastics | Nylon 6 | Razamid® |
| Huaxia Shenzhou FKM DS2604-1 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| INEOS HDPE T50-200-178 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| OTECH PVC OE7444 - Gasket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| LNP™ LUBRICOMP™ DP003 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |