Capilene® G 70 TF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kf8PLu_Capilene-G-70-TF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® G 70 TF is a nucleated polypropylene homopolymer intended for sheet extrusion and thermoforming applications. CAPILENE ® G 70 TF features: nucleating additive, high stiffness, good transparency, high Heat Distortion Temperature (HDT); short injection cycle time. CAPILENE ® G 70 TF is suitable for: extrusion-thermoforming of thin, stiff and transparent food containers, hot-filled containers; injection molding of technical items. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 38.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 9.0 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- 3 | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 122 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 159 | °C | ISO 306/A, ASTM D1525 4 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm) | 30 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 4715AF | Titan Plastics Compounds Co., Ltd. | Nylon 46 | Titalon® |
| Ultramid® A3K BK00464 | BASF Corporation | Nylon 66 | Ultramid® |
| Luranyl® KR 2460/3-2 | ROMIRA GmbH | PPE+PS | Luranyl® |
| Crastin® SK643FR BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Ultramid® B3GK24 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |