Vyncolit® X680
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KeMeOz_Vyncolit-X680.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X680 is a glass bead and glass fiber reinforced phenolic molding compound with excellent mechanical and thermal properties, higher isotropic properties and good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Apparent Density | 0.67 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.36 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Post Shrinkage | 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.5 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.85 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 13000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 185 | MPa | ISO 178 |
| Compressive Stress | 270 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 188 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.4E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.4E+13 | ohms | IEC 60093 |
| Volume Resistivity | 3.2E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa | |
| Screw Speed | 50 | rpm |
| Injection instructions |
|---|
| Injection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 HI 33 GF BLK | RTP Company | Nylon 66 | RTP |
| Sanren Y180L (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| HiFill® POM CO GF10 CC | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Laticonther 47/1 CP/80 | LATI S.p.A. | PP Copolymer | Laticonther |
| PHOENIX™ 8801 | Phon Tech Industrial Company | TPE | PHOENIX™ |