Sinvicomp SGH5900
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Teknor Apex Asia Pacific PTE. LTD. |
| Trademark: | Sinvicomp |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KdUL5N_Sinvicomp-SGH5900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Sinvicomp" SGH 5900 is an extrusion grade polyvinylchloride compound available in pellet form. Generally used in the production of garden hose. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 340 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability 1(190°C) | > 30 | min | BS 2782 |
| Additional Information |
|---|
| Typical temperature profile for processing SINVICOMP compound is from 160°C to 175°C. The optimum temperatures depend on the type of machine as well as screw design being used to process SINVICOMP.Feeding zone: 150°C ~160°CCompression zone: 160°C~165°CMixing zone: 165°C~170°CNozzle/Die Zone: 170°C~175°C |
| Note Message | |
|---|---|
| 1 . | Congo red |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 GR25 NL HS | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| TEKAMID™ TA210SG15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| ExxonMobil™ LLDPE LL 1002YB Cast | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Pearlbond™ 123 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| OTECH TPE OTO9097 - Profile | OTECH Corporation | TPE | OTECH TPE |