NORYL™ PKN4775F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KcVH9w_NORYL-PKN4775F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include packaging for high performance applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 14.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2120 | MPa | ASTM D638 |
| -- | 2120 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 51.5 | MPa | ASTM D638 |
| Yield | 51.3 | MPa | ISO 527-2/50 |
| Fracture 3 | 47.5 | MPa | ASTM D638 |
| Fracture | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.1 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2/50 |
| Fracture 5 | 35 | % | ASTM D638 |
| Fracture | 29 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2210 | MPa | ASTM D790 |
| -- 7 | 2160 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 82.7 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 78.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 160 | J/m | ASTM D256 |
| 23°C | 270 | J/m | ASTM D256 |
| -30°C 10 | 11 | kJ/m² | ISO 180/1A |
| 23°C 11 | 20 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 39.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 122 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 144 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 2.0E-4 | % | |
| Cylinder Zone 1 Temp. | 204 - 227 | °C | |
| Cylinder Zone 2 Temp. | 216 - 238 | °C | |
| Cylinder Zone 3 Temp. | 238 - 266 | °C | |
| Cylinder Zone 4 Temp. | 238 - 266 | °C | |
| Adapter Temperature | 238 - 266 | °C | |
| Melt Temperature | 266 - 277 | °C | |
| Die Temperature | 238 - 266 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsRoll Stack Temp - Bottom: 104 - 121 °CRoll Stack Temp - Middle: 104 - 121 °CRoll Stack Temp - Top: 104 - 121 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 FR | RTP Company | Nylon 66 | RTP |
| Tecodur® PB70 NL SV20 | Eurotec Engineering Plastics | PBT | Tecodur® |
| Wondel® B BR0G4 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| New-prene™ 8180N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| INEOS PP T00G-00 | INEOS Olefins & Polymers USA | TPO | INEOS PP |