VAMPAMID 66 0023 V0 H GW
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KamKhM_VAMPAMID-66-0023-V0-H-GW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0 at 0,8 mm, PBDE & PBDF free, good electrical features, hinge effect, GWFI 960/1-2, GWIT 775/1-2. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 | % | |
| Across Flow | 1.6 | % | |
| Water Absorption (Saturation) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 200 | °C | ASTM D1525 1 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC1000R resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| HiFill® PA6/6 GB10 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LTP ZW-3206 | Chengdu Letian Plastics Co., Ltd | Acetal (POM) Copolymer | LTP |
| OmniCarb™ PC/PBT 1214 | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |
| 3M™ Dyneon™ Fluoroplastic FEP FLEX6305Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |