Order Products : sales@su-jiao.com
RTP 700 SI 2 Z
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kah7wX_RTP-700-SI-2-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Silicone Lubricated - FDA Compliant Ingredients |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 2.0 to 3.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ASTM D638 |
| Tensile Strength | 19.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Flexural Strength | 20.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 91 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 48.9 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 193 to 232 | °C | |
| Mold Temperature | 21.1 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA66 A306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| K-Prene GHT 55 | Technovinyl Polymers India Ltd. | TPE | K-Prene |
| LEXAN™ LGK4030 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| MAJ'ECO FP204ECEL | AD majoris | PE, Unspecified | MAJ'ECO |
| Hostacom HYS 2009R 105518 | LyondellBasell Industries | PP Homopolymer | Hostacom |