| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KadoTG_Andur-AL-95-AP-Curene-111.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Andur AL95AP is a polyether (PTMG) based prepolymer terminated with aliphatic isocyanates to increase color stability, and give longer pot life. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 96 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 14.2 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 40.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 280 | % | ASTM D412 |
| Bayshore Resilience | 45 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 5.0 - 6.0 | min | |
| Demold Time (100°C) | 20 | min | |
| Post Cure Time | |||
| 21°C | 72 | hr | |
| 100°C | 16 | hr |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 380 pliAverage Split Tear, ASTM D1938: 110 pliStoichiometry Curative Level: 95%Mix Temperature: Andur AL 95 AP: 190°F Curene 111: 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA/ABS Blend 3610/4 GK 10 | TER HELL PLASTIC GMBH | ABS+Nylon | TEREZ PA/ABS |
| 4LAC® 25H20800 | 4Plas | ABS | 4LAC® |
| Fainplast PVC HGKA 87 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| FERREX® GPP20CS70BK | Ferro Corporation | PP, Unspecified | FERREX® |
| LNP™ STAT-KON™ DD0009XP compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |