Chemlon® 113 GHIU BK156
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZtAh1_Chemlon-113-GHIU-BK156.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemlon® 113 GHIU BK156 is a Polyamide 66 (Nylon 66) material filled with 13% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 113 GHIU BK156: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % | |
| Flexural Modulus | 4830 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 214 | °C | ISO 75-2/A |
| Melting Temperature | 257 | °C | ASTM D789 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ISO 1325 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ISO 4589-2 |
| FMVSS Flammability | PASSED | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 257 to 271 | °C | |
| Front Temperature | 263 to 279 | °C | |
| Nozzle Temperature | 263 to 282 | °C | |
| Processing (Melt) Temp | 263 to 282 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6850R B38 | Spartech Polycom | PP, Unspecified | Spartech |
| X-Pro PP 2230 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| Zetpol® 2010H | Zeon Corporation | NBR | Zetpol® |
| INSTRUC PSUGF30HF | Infinity LTL Engineered Compounds | PSU | INSTRUC |
| Karina GRAY PVC COMPOUND 880-18/402-F-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |