CP PRYME® Polystyrene PS100HI-8M
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZWt6h_CP-PRYME-Polystyrene-PS100HI-8M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CP PRYME® Polystyrene PS100HI-8M is a High Impact Polystyrene product. It is available in North America. Primary characteristic: high flow. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 22.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 39.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(3.18 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 82.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.18 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 45 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | 0.25 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9519H | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| RTP ESD A 2800-85A | RTP Company | TPO (POE) | RTP |
| Ultraform® N 2650 Z6 LEV | BASF Corporation | Acetal (POM) Copolymer+PUR | Ultraform® |
| NEXT REGRIND POMC TX90-100RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Karina CLEAR PVC COMPOUND -E 800/208-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |