Arnitel® CM600-V
| Category: | TPC-ES , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZPdPO_Arnitel-CM600-V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Arnitel® CM600-V is a Thermoplastic Copolyester Elastomer (TPC-ES) material. It is available in Asia Pacific, Europe, or North America for extrusion. Important attributes of Arnitel® CM600-V are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 420 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 20.5 | MPa | |
| 5.0% Strain | 16.0 | MPa | |
| 10% Strain | 19.5 | MPa | |
| 50% Strain | 17.5 | MPa | |
| 100% Strain | 16.0 | MPa | |
| Nominal Tensile Strain at Break | 200 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | No Break | ISO 179/1eA | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 9.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 205 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.20 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.016 | ||
| 1 MHz | 0.039 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (0.750 mm) | V-2 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP LPP30BD16BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Flexalloy® 9300-80 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Huafon HF-3060D | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Hostacom TKC 151P | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| Sylvin 8495-65 Grey 9618 | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |