ENFLEX V1045D
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | ENPLAST Americas, a Ravago Group Company |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZLCdx_ENFLEX-V1045D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Enflex V1045D TPV (thermoplastic vulcanizate) is a general purpose semi-rigid black EPDM/PP compound available in both natural and black. This grade is design for injection molding, extrusion and blow molding applications requiring moderate rigidity with high heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D, 5 seconds, extruded | 44 | ASTM D2240 | |
| Shore D, 5 seconds, injection molding | 46 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 10.1 | MPa | ASTM D412 |
| Tensile Strength (Break) | 21.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 650 | % | ASTM D412 |
| Tear Strength 1 | 89.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 70°C, 22 hr | 60 | % | ASTM D395 |
| 125°C, 70 hr | 85 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -40.0 | °C | ASTM D746 |
| Melting Temperature | 158 | °C | ASTM D1238 |
| Dynamic Service Temperature | 130 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 182 - 193 | °C | |
| Front Temperature | 188 - 199 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 10.0 - 48.9 | °C | |
| Injection Pressure | 5.17 - 8.96 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² | |
| Cushion | 5.08 - 12.7 | mm |
| Injection instructions |
|---|
| Holding Time: 5 to 7 Sec.Cooling Time: 30 to 50 Sec. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 160 - 177 | °C | |
| Cylinder Zone 1 Temp. | 171 - 191 | °C | |
| Cylinder Zone 2 Temp. | 171 - 191 | °C | |
| Cylinder Zone 3 Temp. | 171 - 191 | °C | |
| Cylinder Zone 4 Temp. | 171 - 191 | °C | |
| Cylinder Zone 5 Temp. | 171 - 191 | °C | |
| Adapter Temperature | 191 - 210 | °C | |
| Melt Temperature | 191 - 199 | °C | |
| Die Temperature | 191 - 210 | °C |
| Extrusion instructions |
|---|
| Screw: L/D 20:1 or greater (L/D 24:1 preferred)Compression Zone: 355 - 390°F (180 - 200°C)Metering Zone: 375 to 410°F (190 to 210°C)Cooling Water: 60 - 85°F (15 - 30°C)Screw Speed: 100 - 200 rpmScreen Pack: 20/40/60 |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prisma® 2400 | Braskem | PP Random Copolymer | Prisma® |
| BESTNYL SE00VI01AS08 | Triesa Plastics | Nylon 66 | BESTNYL |
| Franprene ATA 2250 | Franplast S.r.l. | SBS | Franprene |
| Karina BEIGE PVC COMPOUND -E 828-08/497-Y-RT | Karina Ind. e Com. de Pl谩sticos Ltda | PVC, Unspecified | Karina |
| SABIC® PPcompound 2609B | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |