INEOS LDPE 21H460
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KYkvIy_INEOS-LDPE-21H460.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
21H460 is suitable for a variety of general-purpose packaging films, liners, carrier bags, fine shrink film. 21H460 is an autoclave LDPE homopolymer. It offers the following properties:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | > 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% secant, MD : 50 µm, blown film | 140 | MPa | ISO 1184 |
| 1% secant, TD : 50 µm, blown film | 150 | MPa | ISO 1184 |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 50 µm, blown film | 10.0 | MPa | ISO 1184 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ISO 1184 |
| MD : 50 µm, blown film | 22.0 | MPa | ISO 1184 |
| TD : 50 µm, blown film | 21.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 50 µm, blown film | 400 | % | ISO 1184 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 1184 |
| Dart Drop Impact (50 µm, Blown Film) | 120 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 6.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm film, 2.5:1 blow up ratio, 180°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM 5502-01ST | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Borcell™ HE1344 | Borealis AG | HDPE | Borcell™ |
| Globalene® PC366-4 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| LNP™ THERMOCOMP™ MF002AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| Sylvin 8773-60D White 1403 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |