GLAMIDE® T-400G15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KYAZ11_GLAMIDE-T-400G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE® T-400G15 is a Polyamide 6 (Nylon 6) product filled with 15% glass fiber. It is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.25 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 25 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.50 to 0.70 | -- | % | |
| 3.00 mm | 0.70 to 1.1 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.4 | -- | % | |
| Equilibrium, 65% RH | 3.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 145 | 120 | MPa | |
| Yield, 23°C | 120 | 60.0 | MPa | |
| Yield, 80°C | 50.0 | 35.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 4.0 | 9.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 6700 | 5600 | MPa | |
| 23°C | 5400 | 2700 | MPa | |
| 80°C | 2300 | 1700 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 210 | 100 | MPa | |
| Yield, 23°C | 170 | 80.0 | MPa | |
| Yield, 80°C | 85.0 | 45.0 | MPa | |
| Compressive Strength (23°C) | 110 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 45 | 55 | J/m | |
| 23°C | 64 | 80 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 217 | -- | °C | |
| 1.8 MPa, Unannealed | 178 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 23 | 17 | kV/mm | ASTM D149 |
| Arc Resistance | 110 | 90.0 | sec | ASTM D495 |
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 to 55.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE6205B | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Sindustris PP HI5206R | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Vi-Chem PVC VNC80-30 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Alcryn® 2070 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| Karina IVORY PVC COMPOUND -E ML-IS-FLEX-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |