Vydyne® R862H BK0676
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KXwacz_Vydyne-R862H-BK0676.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R862H BK0676 is a general-purpose, glass fiber and mineral-reinforced, heat-stabilized PA66 resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance. Glass fiber and mineral-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Typical Applications/End Uses: Vydyne R862H BK0676 can be successfully used in a wide range of injection-molding engineering applications. Typical parts include lower cowl top covers, radiator shrouds, fans and mirror brackets, cylinder head covers; and industrial applications such as gears, bearing shells, covers and housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 1.1 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | 7800 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 149 | 98.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.2 | 2.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10800 | 5600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | 120 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 6.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 46 | 50 | kJ/m² | |
| 23°C | 49 | 48 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 6.0 | 7.0 | kJ/m² | |
| 23°C | 7.0 | 11 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 234 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 1.9E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 6.7E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 TFE 10 SI 2 | RTP Company | ABS | RTP |
| S&E General Purpose G-95-045G | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E General Purpose |
| Wanthane® WHT-7190 | Wanhua Chemical Group Co., Ltd. | PC+TPU | Wanthane® |
| Witcom POM-C 2005/130 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Epocast 89537-A/B | Huntsman Advanced Materials | Epoxy | Epocast |