Kelon® A FR H2 CETG/300-V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KVuzMY_Kelon-A-FR-H2-CETG-300-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Heat stabilised. Mineral filler / Glass fibres. UL94 V-0 classified, with halogens, PBB/PBDE and antimonium trioxide free. Product UL certified. Low thermal expansion coefficient. Very high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.2 | % | |
| Flow : 2.00 mm | 0.90 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 10200 | MPa | |
| 60°C | 8000 | MPa | |
| 90°C | 4800 | MPa | |
| 120°C | 3300 | MPa | |
| 150°C | 2800 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 90°C | 40.0 | MPa | |
| Yield, 120°C | 30.0 | MPa | |
| Yield, 150°C | 25.0 | MPa | |
| Break, 23°C | 80.0 | MPa | |
| Break, 60°C | 65.0 | MPa | |
| Break, 90°C | 45.0 | MPa | |
| Break, 120°C | 35.0 | MPa | |
| Break, 150°C | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 90°C | 5.0 | % | |
| Yield, 120°C | 7.0 | % | |
| Yield, 150°C | 10 | % | |
| Break, 23°C | 1.6 | % | |
| Break, 60°C | 2.7 | % | |
| Break, 90°C | 7.0 | % | |
| Break, 120°C | 12 | % | |
| Break, 150°C | 20 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 20 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 115 | °C | |
| Vicat Softening Temperature | 235 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 775 | °C | |
| Oxygen Index | 36 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B1 GF 10 | Plastcom | PBT | SLOVASTER® |
| BP RPP 3015 T NAT | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| Geon™ Specialty Suspension CG E 24 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |
| Geon™ Vinyl Rigid Extrusion L0678 Natural | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| MAJORIS BG164 | AD majoris | PP, Unspecified | MAJORIS |