Karina IVORY PVC COMPOUND 750-35/1-F-IS
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KVThAQ_Karina-IVORY-PVC-COMPOUND-750-35-1-F-IS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.42 to 1.46 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Delta E | < 1.50 | ME 12 | |
| Lead Content | < 100 | ppm | IEC 62321 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 73 to 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 6.86 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 200 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -15.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 2 | > 1.0E+13 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Accura® Bluestone™ | 3D Systems | Unspecified | Accura® |
| DynaMix Lite™ 2244-GHI | Polymer Dynamix | Nylon 12 | DynaMix Lite™ |
| KOPELEN JSS-370N | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| LUVOCOM® 1850/PL/15/BK | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Sarlink® TPE OM-1354 | Teknor Apex Company | TPE | Sarlink® TPE |