LNP™ THERMOCOMP™ PF006 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KVKlwY_LNP-THERMOCOMP-PF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF006 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1006 Product reorder name: PF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.17 to 0.50 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.86 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8760 | MPa | ASTM D638 |
| -- | 8580 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 130 | MPa | ASTM D638 |
| Break | 128 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.8 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6960 | MPa | ASTM D790 |
| -- | 7970 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 201 | MPa | ASTM D790 |
| -- | 204 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 8.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 830 | J/m | ASTM D4812 |
| 23°C 3 | 55 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.10 | J | ASTM D3763 |
| -- | 2.68 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 219 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 206 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 203 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 Z | RTP Company | PC | RTP |
| SHIN-A SCT-150M70 | SHIN-A T&C | Epoxy | SHIN-A |
| TAROMID A 280 G8 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| THORNEL® VMX-24 | Cytec Industries Inc. | Carbon/Epoxy | THORNEL® |
| HI-ZEX™ 8800B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |