Reny® 4011
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KV9QQN_Reny-4011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 4011 is a Polyarylamide (PARA) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 4011 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.66 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 6.3 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 4.50 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.32 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.090 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 21600 | 18600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 152 | 143 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | 1.1 | % | ISO 527-2 |
| Flexural Modulus | 19800 | 19100 | MPa | ISO 178 |
| Flexural Stress | 235 | 228 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.3 | 7.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 16 | 16 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 235 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 226 | 216 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+5 | 3.0E+6 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+4 | 6.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LLDPE UN324 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Edistir® RK 451G | Versalis S.p.A. | PS (HIPS) | Edistir® |
| OMIKRON ML 71 BG NERO | TECNOPOL | PP Homopolymer | OMIKRON |
| Sylvin 5175-92 Green 3154 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 3290-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |