SABIC® PPcompound 31T1010 is a 10% talc-filled polypropylene copolymer for general purpose applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (24 hr) | 1.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1620 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 23.0 | MPa | ISO 527-2/50 |
| Break | 14.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 51 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm Span) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2 | ISO 180/1A | ||
| -20°C | 6.0 | kJ/m² | |
| 0°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed | 107 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Coefficient of Linear Thermal Expansion - Flow (-30 to 100°C) | 84.0 | µm/Mk | ISO 11359-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 10 | % | ASTM D229 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 |
| 3 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® FC 19 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Nipol® NBR N30L | Zeon Corporation | NBR | Nipol® NBR |
| Bayblend® T85 HG | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| APEX® 87-L260M-4 | Teknor Apex Company | PVC, Flexible | APEX® |
| Kepital® F20-52SM | KEP Americas | Acetal (POM) Copolymer | Kepital® |