Fibremod™ GB364WG
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KULdOZ_Fibremod-GB364WG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GB364WG is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in natural but other colours can be provided on request. This material shows excellent mechanical properties also at elevated temperatures. Applications: Fibremod GB364WG has been developed especially for applications like:
Features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 1.1 | % | Internal method |
| Flow direction : 2.00mm | 0.20 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 112 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 6900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 3.3 | % | ISO 527-2/50 |
| Flexural Modulus 2(Injection Molded) | 6000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 49 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 58 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 8.5 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 159 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 143 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 164 | °C | ISO 306/A50 |
| -- | 135 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack pressure: As low as possibleScrew speed: Low to mediumFlow front speed: 100 to 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 mm |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3405-3 | RTP Company | LCP | RTP |
| SILPURAN® 2110 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Chemical Resources PC2200 | Chemical Resources, Inc. | PC | Chemical Resources |
| POLYfill PPC GF5020 | Polykemi AB | PP Copolymer | POLYfill |
| MACOMASS PVC MM-PVC Reg | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |