Amodel® AS-1935 HS Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C). Former PXM-12091 Black: AS-1935 HS BK 328

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Rigid, good High strength frost resistance Good creep resistance Good chemical resistance Heat resistance, high Ethylene glycol resistance Thermal Stability
Uses	Power/other tools Valve/valve components Industrial components Industrial application Thick wall fittings (parts) Machine/mechanical parts Metal substitution Parts under the hood of a car Application in Automobile Field Shell
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.49	g/cm³	ISO 1183/A
Molding Shrinkage			ASTM D955
Flow	0.20	%	ASTM D955
Transverse flow	0.60	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--	12500	MPa	ASTM D638
--	12600	MPa	ISO 527-2/1A/1
Tensile Strength
Fracture	205	MPa	ASTM D638
Fracture	210	MPa	ISO 527-2
Tensile Elongation (Break)	2.2	%	ASTM D638, ISO 527-2
Flexural Modulus
--	11300	MPa	ASTM D790
--	11500	MPa	ISO 178
Flexural Stress
--	300	MPa	ISO 178
Fracture	275	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	8.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	66	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	65	J/m	ASTM D256
--	8.5	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	290	°C	ISO 75-2/Af
Melting Temperature	323	°C	ISO 11357-3

Injection	Nominal Value	Unit
Drying Temperature	121	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.10	%
Hopper Temperature	79.4	°C
Rear Temperature	313 - 330	°C
Front Temperature	326 - 339	°C
Processing (Melt) Temp	330 - 350	°C
Mold Temperature	150	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KTlfIc_Amodel-AS-1935-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 200.7 H	RTP Company	Nylon 66	RTP
Zythane® 6050D	Alliance Polymers & Services	TPU-Polyether	Zythane®
Expandable PS F21B	INEOS Styrenics International SA	PS (EPS)	Expandable PS
LEXAN™ LUX7169 resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
Zytel® SC310 NC010	DuPont Performance Polymers	Nylon 66	Zytel®