TechnoElast 9090
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | TechnoCompound GmbH |
| Trademark: | TechnoElast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KTZB01_TechnoElast-9090.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The TechnoElast TPE compounds are a new, innovative product range of TechnoCompound based on styrene block copolymers. TechnoElast TPE compounds with adjustable melt flow rates possess good insulation properties, good workability, offer good thermal stability, outstanding absorption characteristics as well as elastic memory. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 14.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 250 | % | ISO 527-2 |
| Additional Information |
|---|
| The value listed as Shore Hardness, ISO 868, was tested in accordance with DIN 53505.The value listed as Tensile Stress at Break, ISO 527-1, -2, was tested in accordance with DIN 53504.The value listed as Tensile Strain at Break, ISO 527-1, -2, was tested in accordance with DIN 53504.Moisture Content, Infared 105°C, 15 min: <0.10%Tensile Strain at Break, DIN 53504: >250% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIRASON™ 68 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| SCHULAFORM® 9 A TF 20 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| SCHULAMID® 66 MW 30 FR 4 K2031 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Nanjing Hongrui PA6 B353 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| ELASTOSIL® LR 3005/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |