PRE-ELEC® ESD 5500
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KTZ1N6_PRE-ELEC-ESD-5500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® ESD 5500 is a static dissipative thermoplastic compound based on polypropylene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 5500 can be injection moulded, extruded, blow moulded and blown into film. Surface resistance values of 1e9 O (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. The products made out of PRE-ELEC® ESD 5500 are washable, reusable and recyclable. PRE-ELEC® ESD 5500 is designed for clean applications with extremely low amount of extractable ions. Typical applications include bins, trays, bottles and bags where permanent ESD protection and high cleanliness are required. These products can be used mainly in electronics packaging, but in many other application areas as well. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.913 | g/cm³ | ASTM D792 |
| -- | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.6 | % | ASTM D955 |
| Flow direction | 1.6 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 4.00 mm | 248 | MPa | ASTM D638 |
| 4.00 mm | 250 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 20.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 15.9 | MPa | ASTM D638 |
| 4.00 mm | 16.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 15 | % | ASTM D638, ISO 527-2 |
| Fracture | 600 | % | ASTM D638 |
| Fracture, 4.00mm | 600 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 4.00 mm) | 12.6 | kJ/m² | ASTM D256 |
| Notched Izod Impact 1(23°C) | 13 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C, 4.00 mm) | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 2(23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 80.0 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, not annealed | 50.0 | °C | ASTM D648A, ISO 75-2/Af |
| Vicat Softening Temperature | 135 | °C | ISO 306/A50, ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Static Decay | |||
| -- | sec | ESD S20.20 | |
| -- | sec | IEC 61340-5-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 4 | UL 94 | ||
| 0.991 mm | HB | UL 94 | |
| 1.00 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 30.0 - 40.0 | °C | |
| Injection Pressure | 60.0 - 80.0 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 210°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 速率 A (50°C/h), 载荷2 (50N) |
| 4 . | RD 524 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-50243 | Teknor Apex Company | TPE | Medalist® |
| Toyolac® 600-309 | Toray Resin Company | ABS | Toyolac® |
| ULTRATRAC® H950 | Haysite Reinforced Plastics | Polyester, TS | ULTRATRAC® |
| Gallonprene® GP210-7509 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Latigray 66-01 CX/50 | LATI S.p.A. | Nylon 66 | Latigray |