VALOX™ ENH8560 resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KTOazL_VALOX-ENH8560-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-Brominated & Non-Chlorinated Flame Retardant, 30% Glass fiber reinforced PBT/PET blend |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.59 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/5.0 kg | 10 | g/10 min | ASTM D1238 |
| 265°C/2.16 kg | 5.0 | g/10 min | ASTM D1238 |
| 250°C/5.0 kg | 11 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 250°C/5.0 kg | 10.0 | cm³/10min | ASTM D1238 |
| 265°C/5.0 kg | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.40 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 166 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 12000 | MPa | ASTM D638 |
| -- | 12000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 103 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2/5 |
| Break 4 | 103 | MPa | ASTM D638 |
| Break | 105 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 1.0 | % | ASTM D638 |
| Yield | 1.0 | % | ISO 527-2/5 |
| Break 6 | 2.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 10000 | MPa | ASTM D790 |
| -- 8 | 10000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 165 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 145 | MPa | ASTM D790 |
| Break, 50.0 mm Span 10 | 145 | MPa | ASTM D790 |
| Flexural Strain at Break 11 | 2.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 30 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 7.0 | kJ/m² | ISO 179/2C |
| 23°C 12 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 0°C | 60 | J/m | ASTM D256 |
| 23°C | 60 | J/m | ASTM D256 |
| -30°C 13 | 7.0 | kJ/m² | ISO 180/1A |
| 0°C 14 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 15 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 400 | J/m | ASTM D4812 |
| 23°C | 450 | J/m | ASTM D4812 |
| -30°C 16 | 27 | kJ/m² | ISO 180/1U |
| 23°C 17 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 210 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 18 | 215 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 196 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 19 | 180 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ASTM D1525 20 |
| -- | 196 | °C | ASTM D1525 21 |
| -- | 215 | °C | ISO 306/A50 |
| -- | 203 | °C | ISO 306/B50 |
| -- | 201 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | |
| Flow : 23 to 150°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.6E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 1.4E-4 | cm/cm/°C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | ASTM D149, IEC 60243-1 | ||
| 0.800 mm, in Oil | 35 | kV/mm | |
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Oil | 8.0 | kV/mm | |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.012 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 425 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index (2.25 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 750 | °C | |
| 2.00 mm | 775 | °C | |
| 3.00 mm | 825 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 155 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 255 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 265 to 275 | °C | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | Rate A (50°C/h), Loading 2 (50 N) |
| 21 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2200 G53 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Ferro PP TPP40AC35WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Gallonprene® GP550-7002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Geon™ Vinyl Rigid Extrusion L7035 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Purell RP270G | LyondellBasell Industries | PP Random Copolymer | Purell |