Formolene® HB5502S1
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KSx1Ro_Formolene-HB5502S1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene® HB5502S1 HDPE resin is designed for applications requiring excellent stiffness and stress crack resistance properties. It may be used as a blow molding resin or sheet extrusion thermoforming resin. Formolene® HB5502S1 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| Compression Molded, F50 | 35.0 | hr | ASTM D1693B |
| 100% Igepal, Compression Molded, F50 | 45.0 | hr | ASTM D1693A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | > 600 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1380 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -84.4 | °C | ASTM D746 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® SMC 0412 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Novalloy-B B1300, B1300F | Daicel Polymer Ltd. | ABS+PBT | Novalloy-B |
| AKROLOY® PA GF 50 natural (2916) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| K-Flex 3370 OR FR | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| Huafon HF-3H95AL-1 | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |