ELITE™ 5400GS
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KSc1gg_ELITE-5400GS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™5400GS reinforced polyethylene resin is made of Dow INSITE™The copolymer produced by technology has excellent impact resistance, excellent tear resistance, tensile resistance and optical properties, and can be used to manufacture high-strength blown films. In addition, ELITE™5400GS reinforced polyethylene resin also integrates unique properties such as low sealing temperature, higher modulus and less likely to block, and can be used for automatic packaging. Purpose:
Compliance:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy 1(51 µm) | 5.50 | J | Internal method |
| Film Puncture Force 2(51 µm) | 107 | N | Internal method |
| secant modulus 3 | ASTM D882 | ||
| 1% secant, MD : 51 µm | 171 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 194 | MPa | ASTM D882 |
| Tensile Strength 4 | ASTM D882 | ||
| MD : Yield, 51 µm | 11.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.2 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 54.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 52.0 | MPa | ASTM D882 |
| Tensile Elongation 5 | ASTM D882 | ||
| MD : Fracture, 51 µm | 640 | % | ASTM D882 |
| TD : Fracture, 51 µm | 660 | % | ASTM D882 |
| Dart Drop Impact 6(51 µm) | > 850 | g | ASTM D1709B |
| Elmendorf Tear Strength 7 | ASTM D1922 | ||
| MD : 51 µm | 630 | g | ASTM D1922 |
| TD : 51 µm | 770 | g | ASTM D1922 |
| Seal Initiation Temperature 8(51 µm) | 90.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 9(20°, 51.0 µm) | 77 | ASTM D2457 | |
| Haze 10(51.0 µm) | 9.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 246 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜挤出的制造条件： 模具间隙：0.8-2.8 mm。 熔体温度：190-246 °C。 放大比：1.5:1 至 3.5:1。 |
| Note Message | |
|---|---|
| 1 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 2 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 3 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 4 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 5 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 6 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 7 . | Type A; Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 8 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. Achieve a temperature of 5.25 N/15mm heat sealing strength. |
| 9 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| 10 . | Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9mm mold gap. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next PMMA AX-01YW.(MH-3121) | Next Polymers Ltd. | Acrylic (PMMA) | Next PMMA |
| Anjatech® 100X-E | Almaak International GmbH | PC | Anjatech® |
| Chemraz 555 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| GAPEX® HPP30GR33NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| InnoPlus HD1600J | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |