Vyncolit® X611
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KSOacG_Vyncolit-X611.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X611 is a glass fiber reinforced phenolic molding compound with excellent mechanical and electrical properties, good dimensional stability, heat and chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Apparent Density | 0.68 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.30 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Post Shrinkage | 0.070 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.4 | % | ISO 178 |
| Tensile Modulus | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.60 | % | ISO 527-2 |
| Flexural Modulus | 14000 | MPa | ISO 178 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Compressive Stress | 270 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 208 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.2E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+13 | ohms | IEC 60093 |
| Volume Resistivity | 7.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 75.0 | °C | |
| Nozzle Temperature | 90.0 | °C | |
| Processing (Melt) Temp | 100 - 115 | °C | |
| Mold Temperature | 165 - 190 | °C | |
| Injection Pressure | 100 - 250 | MPa | |
| Holding Pressure | 30.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw Speed | 50 | rpm |
| Injection instructions |
|---|
| Hold Time: 1 to 5 sec/mmCure Time: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 AR 10 | RTP Company | Nylon 66 | RTP |
| Sarlink® TPE ME-2555B XRD | Teknor Apex Company | TPE | Sarlink® TPE |
| MOSTEN MA 745 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| Elastamax™ XL 0131-59 | PolyOne Corporation | SBC | Elastamax™ |
| Hax™ HFX 505 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |