NOVALAC RX®620 Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
NOVALAC RX®620 is a phenolic (Phenolic) material, and its filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. NOVALAC RX®The main features of the 620 are: flame retardant/rated flame chemical resistance high strength Creep resistance Good dimensional stability Typical application areas include: Electrical/electronic applications engineering/industrial accessories electrical appliances House Tools

General Information
Filler / Reinforcement	Glass fiber reinforced material
Additive	Lubricant
Features	Ultra high toughness Good dimensional stability Low smoke High strength Antibacterial property Solvent resistance Good creep resistance alkali resistance acid resistance Self-lubricating
Uses	Membrane key switch Pump parts Gear Electrical/Electronic Applications Electrical appliances Power/other tools Connector Application in Automobile Field Shell
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.69	g/cm³	ASTM D792, ISO 1183
Bulk Factor	2.6		ASTM D1895
Molding Shrinkage
Flow : Molding	0.20	%	ASTM D955
Flow direction	0.20	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.060	%	ASTM D570, ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (E-Scale)	70		ASTM D785, ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
Fracture	40.0	MPa	ISO 527-2
--	51.7	MPa	ASTM D638
Flexural Modulus
--	17200	MPa	ASTM D790
--	15000	MPa	ISO 178
Flexural Strength
--	114	MPa	ASTM D790
--	70.0	MPa	ISO 178
Compressive Strength	145	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
--	29	J/m	ASTM D256A
--	1.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
1.8 MPa, not annealed	207	°C	ASTM D648
1.8 MPa, not annealed	210	°C	ISO 75-2/A
CLTE - Flow	1.8E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.68	W/m/K	ASTM C177
RTI Elec	150	°C	UL 746
RTI Imp	150	°C	UL 746
RTI	150	°C	UL 746

Flammability	Nominal Value	Test Method
Flame Rating		UL 94
1.59 mm	V-0	UL 94
3.18 mm	V-0	UL 94

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Back Pressure	0.207	MPa

Injection instructions
Plastication: 50rpmInjection Pressure: Set to give 3 to 5 seconds injection timeHold Pressure: 50 to 100% of injection pressureHold Time: 10 sec minimumCure Time, 0.125 in: 30 to 35 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.15%Flexural Strain, ASTM D790: 0.7%DTUL @264psi - Unannealed, ASTM D648, Post Baked: 550°FCompressive Strength, ISO 604: 160 MPaCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Injection instructions

Plastication: 50rpmInjection Pressure: Set to give 3 to 5 seconds injection timeHold Pressure: 50 to 100% of injection pressureHold Time: 10 sec minimumCure Time, 0.125 in: 30 to 35 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577 using compression molded specimens.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.15%Flexural Strain, ASTM D790: 0.7%DTUL @264psi - Unannealed, ASTM D648, Post Baked: 550°FCompressive Strength, ISO 604: 160 MPaCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	NOVALAC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KQm0O2_NOVALAC-RX-620.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene HP510-01UV	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
Michilene F8250-02	API Polymers, Inc.	PP Copolymer	Michilene
Sinvicomp SFW7525D	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
TEKALOY™ T80HI	Mando Advanced Materials Co., Ltd.	ABS+PBT	TEKALOY™
Stanyl® Diablo OCD2305 BM (NC214)	DSM Engineering Plastics	Nylon 46	Stanyl®