PRIME TPO J-5710
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | PRIME TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KQaVvG_PRIME-TPO-J-5710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRIME TPO J-5710 is a Polypropylene Random Copolymer (PP Random Copolymer) product. It is available in Asia Pacific, Europe, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 11.0 | MPa | |
| Break | 17.0 | MPa | |
| Tensile Strain (Break) | < 500 | % | ISO 527-2 |
| Flexural Modulus | 220 | MPa | ISO 178 |
| Flexural Stress | 10.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 80 | µm | |
| Tensile Modulus | JIS Z1702 | ||
| MD : 80 µm | 280 | MPa | |
| TD : 80 µm | 280 | MPa | |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 80 µm | 33.0 | MPa | |
| TD : Break, 80 µm | 33.0 | MPa | |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 80 µm | < 500 | % | |
| TD : Break, 80 µm | < 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | JIS K7105 | ||
| 80.0 µm 1 | 0.40 | % | |
| 80.0 µm 2 | 2.0 | % |
| Note Message | |
|---|---|
| 1 . | Internal |
| 2 . | All |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 281 MS | RTP Company | Nylon 66 | RTP |
| Unilex™ UP 1102C | United Polychem | PP Random Copolymer | Unilex™ |
| AEI SX703:CM488-6 | AEI Compounds Limited | HDPE | AEI |
| Fainplast PVC GK 01359/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina WHITE PVC COMPOUND 750D10/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |