GAPEKK™ 3200G
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | GAPEKK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KPrRGV_GAPEKK-3200G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high performance thermoplastic polymer, unfilled Polyether Ketone Ketone (PEKK), semicrystalline granules suitable for injection molding and stock shapes extrusion, standard flow, Brown in color. Application Areas: Suitable for high temperature applications, with high compressive strength & abrasion resistance, high chemical resistance & oil resistance etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | |
| Molding Shrinkage 1 | |||
| Flow | 1.0 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4000 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 to 15 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 180 | MPa | ASTM D790 |
| Compressive Modulus | 2100 | MPa | ASTM D695 |
| Compressive Strength (23°C) | 132 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 189 | °C | ASTM D648 |
| Continuous Use Temperature | 300 | °C | UL 746B |
| Glass Transition Temperature | 176 | °C | ASTM D3418 |
| Melting Temperature | 396 | °C | ASTM D3418 |
| Thermal Stability - Haake 2 | 20 | min |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 420 | °C | |
| Processing (Melt) Temp | 390 to 420 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 420°C nozzle, 220°C Mold |
| 2 . | GSRF 05/420°C, 60 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vistalon™ 2504 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Complet® LGF40-PA12 | PlastiComp, Inc. | Nylon 12 | Complet® |
| Geon™ Vinyl Flexible B8502 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LUVOCOM® 21-8113 | Lehmann & Voss & Co. | Nylon 6/6T | LUVOCOM® |
| Moplen HP2619A | LyondellBasell Industries | PP Homopolymer | Moplen |