Reslen PPH 30T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polimarky Spolka Jawna |
| Trademark: | Reslen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KPqAsK_Reslen-PPH-30T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reslen PPH 30T is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in Europe. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 to 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 20 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 to 2300 | MPa | ISO 527-2 |
| Tensile Stress | 23.0 to 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 to 100 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 to 5.5 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 68.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Weifang Kingdom CM30B | Weifang Kingdom Plastic Co., Ltd | CM | Weifang Kingdom |
| Borealis PE CA9150 | Borealis AG | LDPE | Borealis PE |
| Karina CLEAR PVC COMPOUND 80/295-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LONGLITE® PBT 4115-201D | CCP Group | PBT | LONGLITE® PBT |
| Sylvin 9710-80FUV Blue 8335 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |