Elexar® EL-1934A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Elexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KOH27v_Elexar-EL-1934A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Elexar®EL-1934A is a styrene-ethylene-butylene-styrene block copolymer (SEBS) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Elexar®The main features of the EL-1934A are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 11.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 550 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| 131°C, 3600 hr | -13 | % | ASTM D573 |
| 136°C, 168 hr | 2.0 | % | ASTM D573 |
| 158°C, 168 hr | -5.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | ASTM D573 | ||
| 131°C, 3600 hr | -15 | % | ASTM D573 |
| 136°C, 168 hr | -8.0 | % | ASTM D573 |
| 158°C, 168 hr | -14 | % | ASTM D573 |
| Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil) | -10 | % | ASTM D471 |
| Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil) | -2.0 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 105 | °C | UL 1581 |
| Brittleness Temperature | < -55.0 | °C | ASTM D746 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 39 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.20 | ASTM D150 | |
| Dissipation Factor | 3.3E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.35 to 1.55mm, All Colors) | V-0 | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 216 | °C | |
| Middle Temperature | 213 - 221 | °C | |
| Front Temperature | 221 - 227 | °C | |
| Nozzle Temperature | 221 - 229 | °C | |
| Processing (Melt) Temp | 221 - 229 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 210 | °C | |
| Cylinder Zone 2 Temp. | 199 - 216 | °C | |
| Cylinder Zone 3 Temp. | 213 - 221 | °C | |
| Cylinder Zone 5 Temp. | 221 - 227 | °C | |
| Die Temperature | 221 - 229 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 6019 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Random Copolymer | POLYPRO® |
| RTP 2800 B-65A Z | RTP Company | TPO (POE) | RTP |
| Bayblend® FR3008 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Epolene® C-13 | Westlake Chemical Corporation | LDPE | Epolene® |
| Lumid® GP2150A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |