Petra® 130
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Petra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KNPYk6_Petra-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate injection molding compound. It is available in natural and pigmented versions. It exhibits a superb combination of performance properties including high strength and stiffness at elevated temperatures with good chemical resistance and dimensional stability. Applications Petra 130 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -40°C | 10400 | MPa | |
| 23°C | 10200 | MPa | |
| 80°C | 4950 | MPa | |
| 121°C | 2940 | MPa | |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Break, -40°C | 210 | MPa | |
| Break, 23°C | 155 | MPa | |
| Break, 80°C | 80.0 | MPa | |
| Break, 121°C | 65.0 | MPa | |
| Tensile Elongation | |||
| Break, 23°C | 3.0 | % | ASTM D638 |
| Break, 23°C | 3.5 | % | ISO 527-2 |
| Flexural Modulus | ASTM D790 | ||
| -40°C | 9660 | MPa | |
| 23°C | 8970 | MPa | |
| 65°C | 6130 | MPa | |
| 90°C | 3440 | MPa | |
| 121°C | 2830 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -40°C | 275 | MPa | |
| 23°C | 240 | MPa | |
| 65°C | 170 | MPa | |
| 90°C | 105 | MPa | |
| 121°C | 85.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Peak Melting Temperature | 245 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 1.50 mm 1 | 22 | kV/mm | ASTM D149 |
| -- | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.020 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 383 SI HF | RTP Company | PC | RTP |
| Shin-Etsu Elastomer FE-381U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Tritan™ EX401 | Eastman Chemical Company | Copolyester | Tritan™ |
| FRAGOM G/458 ES | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |