INSULCAST® 116 FR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KMf0zC_INSULCAST-116-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 116 FR is a one to one ratio (weight or volume) epoxy potting and casting compound designed for production use. The convenient mixing ratio of the material makes it ideal for production line mixing as well as automatic dispensing. INSULCAST 116 FR is among the safest epoxy compounds available. It appreciably reduces the risk of eye, skin or respiratory problems generally associated with the use of epoxy compounds. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Compressive Strength | 86.2 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 3.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.43 | W/m/K | |
| Heat Deflection Temperature | 70 | °C | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.40 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Black | ||
| -- 2 | Grey | ||
| Density | |||
| -- 3 | 1.45 | g/cm³ | |
| -- 4 | 1.50 | g/cm³ | |
| Viscosity | |||
| -- 5 | 7.2 | Pa·s | ASTM D2393 |
| -- 6 | 8.1 | Pa·s | |
| -- 7 | 11 | Pa·s | ASTM D2393 |
| Curing Time (22°C) | 16 to 24 | hr | |
| Gel Time (25°C) | 1.8E+2 to 2.4E+2 | min | |
| Pot Life 8 | 90 | min |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part A |
| 6 . | Mixed |
| 7 . | Part B |
| 8 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 HF PRTA011 PR311 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| 3M™ Dyneon™ PTFE TF 2021Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| AlphaSeal™ 255 H | AlphaGary | TPE | AlphaSeal™ |
| Karina IVORY PVC COMPOUND 700-35/ 1-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLANAC BT-2215 | TOYOBO America, Inc. | PBT | PLANAC |