Tenite™ Butyrate 285A2R30018 Natural, Trsp
| Category: | CAB , Cellulose Acetate Butyrate |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tenite™ Butyrate |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KMGiVv_Tenite-Butyrate-285A2R30018-Natural-Trsp.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulose plastics are available in natural, clear, selected ambers, or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-18 has a plasticizer level of 18% and contains an odor mask. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 26 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 23.5 | MPa | |
| Break, 23°C | 30.7 | MPa | |
| Tensile Elongation (Break, 23°C) | 50 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1030 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 30.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 110 | J/m | |
| 23°C | 360 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 75.0 | °C | |
| 1.8 MPa, Annealed | 61.0 | °C | |
| Vicat Softening Temperature 2 | 94.0 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soluble Matter Loss (23°C) | 0.10 | % | ASTM D570 |
| Weight Loss on Heating - 72 hrs (80°C) | 0.90 | % | ASTM D707 |
| Note Message | |
|---|---|
| 1 . | Conditioned 4 hours at 70°C (158°F) |
| 2 . | Conditioned 4 hours at 70°C (158°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net VC710 | Polytech & Net Gmbh | EVA | Polytech & Net |
| Staramide PF006ES | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Supersoft Actymer® AE-2000S | Riken Technos Corp. | TPV | Supersoft Actymer® |
| Delrin® SC631 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Hostaform® MT8U05 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |