Torlon® 4200
| Category: | PAI , Polyamide-imide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Torlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KKlHBP_Torlon-4200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Torlon® 4200 is an unreinforced, unpigmented grade of polyamide-imide (PAI) resin for extrusion. This grade is designed for applications in the semiconductor industry which cannot tolerate particulates such as metals or inorganic particles migrating from the polymer. Torlon® 4200 has the best impact resistance and greatest elongation of all the Torlon® grades. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.85 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.33 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 4900 | MPa | ASTM D1708 |
| -- 1 | 4480 | MPa | ASTM D638 |
| Tensile Strength 2 | 152 | MPa | ASTM D638 |
| Tensile Stress | 192 | MPa | ASTM D1708 |
| Tensile Elongation | |||
| Break | 15 | % | ASTM D1708 |
| Break 3 | 7.6 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 5030 | MPa | |
| 232°C | 3590 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 23°C | 241 | MPa | |
| 232°C | 118 | MPa | |
| Compressive Modulus | 4000 | MPa | ASTM D695 |
| Compressive Strength | 221 | MPa | ASTM D695 |
| Poisson's Ratio | 0.45 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 278 | °C | ASTM D648 |
| CLTE - Flow | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.26 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+18 | ohms | ASTM D257 |
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 4.20 | ||
| 1 MHz | 3.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 0.026 | ||
| 1 MHz | 0.031 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 304 | °C | |
| Nozzle Temperature | 371 | °C | |
| Mold Temperature | 199 to 216 | °C | |
| Back Pressure | 6.89 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Screw L/D Ratio | 18.0:1.0 to 24.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Type I |
| 2 . | Type I |
| 3 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound 3025GNH15 | Samyang Corporation | PC | TRIREX® Compound |
| DOW™ HDPE 7808 C | The Dow Chemical Company | HDPE | DOW™ HDPE |
| UNITIKA Nylon 6 A1030GFL | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| LNP™ KONDUIT™ PX11313 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |
| Shida 020 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |