NYCOA Polyamide ASN 27 300 KNF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KKgPKA_NYCOA-Polyamide-ASN-27-300-KNF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA ASN 27/300 KNF is a 30% glass fiber reinforced, heat stabilized Nylon 6 resin used for injection molding. This grade features excellent strength and stiffness, dimensional stability, and a greater service life than standard grades of glass reinforce NYCOA ASN 27/300 KNF is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. Typical applications include automotive pedals, power tool housing, and lawn & garden equipment parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 9450 | MPa | ASTM D638 |
| Tensile Strength 2 | 178 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 8220 | MPa | ASTM D790 |
| Flexural Strength 5 | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Melting Temperature | 222 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 243 - 282 | °C | |
| Front Temperature | 254 - 291 | °C | |
| Nozzle Temperature | 252 - 291 | °C | |
| Processing (Melt) Temp | 254 - 291 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Industrial Series PG30-02BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Industrial Series |
| ALTECH® PA66 A 2025/109 GF25 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| OmniLon™ PA6/6 U GR13 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Pemex BDL 92020 C | Pemex Petroquímica | LLDPE | Pemex |
| MACOMASS PP MM-PP Reg | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |