| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Tyne Plastics LLC. |
| Trademark: | TYLON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KKWNkT_TYLON-8433L.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Data was measured on natural colored test specimens. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 254 | °C | |
| 1.8 MPa, Unannealed | 249 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 30YK270 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Sipolprene® 46185 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| SUMIKASUPER® LCP E4006L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| TEREZ PC 1007 GF 10 | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| APEX® 1523E-8 | Teknor Apex Company | PVC, Flexible | APEX® |