Miramid® DB1515C
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Leuna GmbH |
| Trademark: | Miramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KIvFZr_Miramid-DB1515C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Miramid® DB1515C is a Polyamide 6 (Nylon 6) material filled with filler. It is available in Europe for injection molding. Primary attribute of Miramid® DB1515C: Mold Release Agent. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1350 | -- | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | |||
| Saturation | 6.0 | -- | % | |
| Equilibrium | 1.8 | -- | % | |
| Viscosity number | 150 | -- | cm³/g | ISO 307, 1157, 1628 3 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 6200 | 3700 | MPa | ISO 527-2 4 |
| Tensile Stress (Break) | 120 | 70.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Break) | 3.0 | 6.5 | % | ISO 527-2 6 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | |||
| -30°C | 5.00 | -- | kJ/m² | |
| 23°C | 6.00 | 9.00 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 8 | |||
| -30°C | 45.0 | -- | kJ/m² | |
| 23°C | 45.0 | 60.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 9 | |||
| 0.45 MPa | 215 | -- | °C | |
| 1.8 MPa | 200 | -- | °C | |
| Melting Temperature 10 | 220 | -- | °C | ISO 11357-3 11 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume resistivity | 1.0E+13 | 1.0E+10 | ohms·m | IEC 60093 12 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 13 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 10 °C/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 3000-70A | Vi-Chem Corporation | TPE | Sevrene® |
| SNOLEN® EF 2.1/46 T | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| NEOFLON™ M-300H | Daikin Fluorochemicals (China) Co., Ltd. | PCTFE | NEOFLON™ |
| Latilub 57D-15T G/30 | LATI S.p.A. | Nylon, Unspecified | Latilub |
| POCAN® KL 1-7033 000000 | LANXESS GmbH | PBT | POCAN® |