Akulon® K222-DL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KITrZK_Akulon-K222-DL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K222-DL is a Polyamide 6 (Nylon 6) material. It is available in North America. Important attributes of Akulon® K222-DL are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3800 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 95.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 15 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2600 | -- | MPa | ISO 178 |
| Flexural Stress | 100 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 8.0 | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 9.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.0E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | V-2 | -- | IEC 60695-11-10, -20 | |
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FE-361TU | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Next Nylon 66 Prime Series PG15-01BL | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| FHR Polypropylene P9H8M-015 | Flint Hills Resources, LP | PP, Unspecified | FHR Polypropylene |
| Fixmaster Wear Resistant Putty | Loctite® | Epoxy | Fixmaster |
| MAJORIS CW337 - 7731 | AD majoris | PP Homopolymer | MAJORIS |