Durethan® BG 30 X F30 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KI0Q1v_DurethanBG30XF30000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers/glass spheres, injection molding, flame retardant, low tendency to warp, improved surface finish |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.63 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.88 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.70 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.40 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | -- | % | ISO 2577 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 210 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7500 | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 105 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.7 | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7300 | 4200 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 175 | 120 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.8 | 4.2 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFHR, 14-080, (GF+GB) 30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 30 | 35 | kJ/m² | ISO 180/1U |
| 23°C | 40 | 45 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.80 | -- | J | ISO 6603-2 |
| 23°C | 2.40 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 550 | -- | N | ISO 6603-2 |
| 23°C | 650 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 185 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 33 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 1 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | V-0 | -- | UL 94 | |
| 1.50 mm | V-0 | -- | UL 94 | |
| 3.00 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 825 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 800 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 825 | -- | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 32 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3561 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 207 TFE 13 SI 2 | RTP Company | Nylon 66 | RTP |
| Surlyn® 1901 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| APEX® 3611-65 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina WHITE PVC COMPOUND 806-10/236-H-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |